Superlite
TECHNICAL DATA SHEET Material Composition:
Factors affecting on the gasket Areas of application
SUPERLITE
Chrysotile asbestos fibre, Mineral Fibre, Natural Rubber and NBR. General properties and applications : To seal off steam, water, air, saline solutions, alkalies, ammonia under low service conditions.
The suitability of a gasket material for an application is dependent upon a multiplicity of factors as shown in the above digram. Max. temperature and pressure values can
This area refer , the gasket material is normally suitable subject to chemical compatibility.
Dimensions of standard sheets :
1500 X 4000 mm, 1500 X 2000 mm, 1300 X 3900 mm, 1270 X 1270 mm, 2100 X 3000 mm, 1500 X 3000 mm.
Specification: IS 2712:1998 Grade: W/3 COMPLIANCE: ASTM:F104 F 112000 M4 Finish : Grey / Graphited (other Colour on Customer requirement). Technical data The following information applies to material thickness 1.5 mm . Test method Specified Value Unit Max. Operating Temperature 440 °C Max. Operating Pressure 80 Kg/cm² Density ASTM F 1315 1.7 -2.20 g/cm³ Compressibility ASTM F 36 A 6 - 14 % Recovery ASTM F 36 A ≥ 40.0 % Tensile Strength ASTM F 152 ≥ 7.5 N/mm² Loss on ignition ASTM F 495 ≤ 28 % Flexibility No Cracks -
Standard sheet sizes :1500 X 1500 mm,1500 X 2250mm, 1500 X 4500 mm ,1500 X 1000 mm,1000X1000 mm
ASTM F 147 B All information and recommendations given in this brochure are correct to the best of our knowledge. However, in view of the wide varity of possible installation and operating conditions one cannot draw the final conclusion in all application cases regarding the behaviour in a gasket joint. Therefore, information can only serve as a guideline.
above digram. Max. temperature and pressure values can not define the suitability for application. It is always advisable to consider these factors when selecting a material for a given application . This area refer, the gasket material may be suitable but a technical support is recommended. This area refer, do not install the gasket without technical evaluation.